Sealing Ability of ProRoot MTA and MTA-Angelus Simulating a One-Step Apical Barrier Technique- An in vitro Study

Endodontic treatment of the pulpless tooth with an immature root apex poses a special challenge for the clinician due to lack of an apical stop against which to compact an interim dressing of calcium hydroxide, or the final obturation material. A one-visit apexification protocol with MTA (Mineral Trioxide Aggregate) has be seen as an alternative to the traditional treatment practices with calcium hydroxide [Ca(OH)2]. The aim of this study was to investigate the use of MTA as a 5mm apical barrier by comparing sealing ability of ProRoot MTA to that of MTA-Angelus. 50 freshly extracted Maxillary and Mandibular single canal sound human incisor teeth were used in this study, which were decoronated to standardized 10mm root lengths. The root segments were prepared to simulate the clinical situation of an open apex with Gates Glidden burs # 5-1 and randomly assigned into 2 experimental groups of 20 samples each (Group A: ProRoot MTA, Group B: MTA-Angelus) and 10 root segments were used as control (Group C) where no apical barrier was used. After obturation the coronal portion of all samples were sealed with Glass Ionomer and stored at 37°C and 100% humidity for 4 weeks. The root segments were then double coated with nail varnish except for the apical 1mm and apical ends of all root segments were suspended vertically in methylene blue dye for 48 hours at room temperature. After removal from the dye, the samples were sectioned longitudinally and linear dye penetration was measured using a Grid and stereomicroscope. The measurements were tabulated and statistically analyzed. The mean percentage of dye leakage for Group A was 55.5% and for Group B was 53.25%. The results showed no statistically significant difference in the sealing ability of ProRoot MTA and MTA-Angelus when used as apical barriers.

mineral trioxide aggregate, apexification, apical barrier

1. Steinig TH, Regan JD, Gutmann JL. The use and predictable placement of Mineral Trioxide Aggregate in one-visit apexification cases. Aust Endod J, 29(1): 34–42, 2003.

2. Matt GD, Thorpe JR, Strother JM and McClanahan SB. Comparative Study Of White And Gray Mineral Trioxide Aggregate (MTA) Simu-lating a One- or Two-Step Apical Barrier Technique. J Endodon, 30(12): 876–879, 2004.

3. Rafter M. Apexification: a review. Dent Traumatol, 21: 1–8, 2005.

4. Ham KA, Witherspoon DE, Gutmann JL, Ravindranath S, Gait TC, Opperman LA. Preliminary Evaluation of BMP-2 Expression and His-tological charachteristics During Apexification with Calcium Hydrox-ide and Mineral Trioxide Aggregate. JOE, 31(4): 275–279, 2005.

5. Pradhan DP, Chawla HS, Gauba K, Goyal A. Comparative Evaluation of Endodontic Management of Teeth With Unformed Apices With Min-eral Trioxide Aggregate and Calcium Hydroxide. Journal of Dentistry for Children, 73(2): 79–85, 2006.

6. Harbert H. Generic Tricalcium Phosphate Plugs: An Adjunct in Endodontics. J Endodon, 17(3): 131–4, 1991.

7. Andreasen JO, Farik B, Munksgaard EC. Long-term calcium hydroxide as a root canal dressing may increase risk of root fracture. Dental Trau-matology, 18: 134–7, 2002.

8. Felippe WT, Felippe MCS, Rocha MJC. The effect of mineral trioxide aggregate on the apexification and periapical healing of teeth with incomplete root formation. International Endodontic Journal, 39: 2–9, 2006.

9. Ripamonti U, Reddi AH. Tissue engineering, morphogenesis and regeneration of the periodontal tissues by bone morphogenetic proteins. Crit Rev Oral Biol Med, 8: 154–63, 1997.

10. Stewart DJ. Root canal therapy in incisor teeth with open apices. Br Dent J, 114: 249, 1963.

11. Friend LA. The root treatment of teeth with open apices. Proc R Soc Med, 19: 1035–6, 1966.

12. Kaiser HJ. Management of wide open apex canals with calcium hydroxide. Presented at the 21st Annual Meeting of the American Asso-ciation of Endodontists, Washington DC, April 17 1964.

13. Frank AL. Therapy for the divergent pulpless tooth by continued apical formation. J Am Dent Assoc, 72: 87–93, 1966.

14. Coviello J, Brilliant JD. A preliminary clinical study on the use of tri-calcium phosphate as an apical barrier. J Endodon, 5: 6–13, 1979.

15. Pitts Dl, Jones EL, Oswald RJ. A histological comparison of calcium hydroxide plugs and dentin plugs used for the control of gutta percha root canal filling material. J Endodon, 10: 283–93, 1984.

16. Hammarstrom LE, Blomlof LB, Feiglin B, Lindskog SF. Effect of calicum hydroxide treatment on periodontal repair and root resorption. Endod Dent Traumatol, 2: 184–189, 1986.

17. Al-Kahtani A, Shostad S, Schifferle R and Bhambani S. In vitro Eval-uation of an Orthograde Apical Plug of MTA in Permanent Teeth with Simulated Immature Apices. J Endodon, 31(2): 117–119, 2005.

18. Torabinejad M, Pitt Ford TR. Root end filling materials: a review. Endod Dent Traumatol, 12: 161–178, 1996.

19. Villa P, Ferna´ndez R. Apexification of a replanted tooth using mineral trioxide aggregate. Dent Traumatol, 21: 306–308, 2005.

20. Duarte MAH, Demarchi ACCO, Yamashita JC, Kuga MC, Fraga SC. pH and calcium ion release of 2 root end filling materials. Oral Surg Oral Pathol Oral Med, 95: 345–7, 2003.

21. Menezes R, Bramante CM, Letra A, Carvalho VGG, Garcia RB. Histo-logic evaluation of pulpotomies in dog using two types of mineral tri-oxide aggregate and regular and white Portland cements as wound dressings. Oral Surg Oral Pathol Oral Med, 98: 376–9, 2004.

22. Torabinejad M, Hong CU, Mc Donald F and Ford TRP. Physical and Chemical Properties of a New Root-End Filling Material. J Endodon, 21(7): 349–353, 1995.

23. MTA-Angelus instruction manual. Angelus Dental Solutions. From the website: www.angelus.in.br

24. Parirokh M, Asgary S, Eghbal MJ, Stowe S, Eslami B, Eskandarizade A, Shabahang S. A comparative study of white and grey mineral triox-ide aggregate as pulp capping agents in dog’s teeth. Dent Traumatol, 21: 150–154, 2005.

25. Bozeman TZ, Lemon R, Eleazer PD, XU X. To compare the elemental dissolution characteristics and crystal growth characteristics of gray Mineral Trioxide Aggregate (MTA), white MTA, and an experimental material called Dentalcrete. J Endod, 32(5): 425–8, 2006.

26. Casella G, Ferlito S. The use of mineral trioxide aggregate in endodon-tics. Minerva Stomatol, 55(3): 123–43, 2006.

27. Goodell GG, Morl RO, Hutter JW, Nicoll BK. Linear dye penetration of a calcium phosphate cement apical barrier. J Endodon, 23(3): 174–177, 1997.